中性子イメージングによる純パラジウムおよびアルミニウム合金中の水素濃度解析

清水 一行*; 林田 洋寿*; 戸田 裕之*; 甲斐 哲也; 松本 吉弘*; 松本 佳久*

日本金属学会誌, 83(11), p.434 - 440, 2019/11

https://doi.org/10.2320/jinstmet.J2019016

Neutron imaging experiment was performed to visualize the distribution of solute hydrogen in an Al-10.1%Zn-1.2%Mg alloy and a pure palladium after hydrogen charging. Changes in the contrast of neutron transmission images caused by hydrogen were clearly observed in a palladium. In the wavelength range of 2-3 AA and 5-13.5 AA, the mean neutron transmission around the center of a hydrogen-charged palladium were 0.692 and 0.511, respectively. The hydrogen content in a palladium was estimated to be 10.8 mol% from the measured neutron transmission. This study has demonstrated that hydrogen content can be analyzed by considering the wavelength dependence of neutron intensity. On the other hand, hydrogen could not be observed from the neutron transmission image in Al-Zn-Mg alloys. This was due to the low hydrogen content, which was mass ppm level even after hydrogen charging, and statistical precision was not sufficient to discuss the amount of hydrogen of the mass ppm order.